Journal
BIOMATERIALS
Volume 26, Issue 9, Pages 1035-1042Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.biomaterials.2004.04.003
Keywords
interfibrillar spaces; self-etch adhesives; incomplete resin infiltration
Funding
- NIDCR NIH HHS [DE 014911, DE 015306] Funding Source: Medline
Ask authors/readers for more resources
This study provided morphological evidence that discrepancies between the depth of demineralisation and the depth of resin infiltration can occur in some mild self-etch adhesives. Sound dentine specimens derived from extracted human third molars were bonded with 5 one-step and 5 two-step self-etch adhesives. One millimeter thick slabs containing the resin-dentine interfaces were immersed in 50wt% aqueous ammoniacal silver nitrate and processed for TEM examination. A zone of partially etched but uninfiltrated dentine was identified beneath the hybrid layers in the milder versions of both one-step and two-step self-etch adhesives. This zone was characterised by the occurrence of silver deposits along the interfibrillar spaces of mineralised collagen fibrils. The silver infiltrated interfibrillar spaces were clearly identified from the one-step self-etch adhesives Xeno III, iBond, Brush&Bond and the experimental adhesive, and were thinner and only occasionally observed in the two-step self-etch adhesives Clearfil SE Bond and Clearfil Protect Bond. The more aggressive one-step and two-step adhesives that exhibit more abrupt transitions from completely demineralised to mineralised dentin were devoid of these silver-infiltrated interfibrillar spaces beneath the hybrid layers. Incomplete resin infiltration observed in some self-etch adhesives may be caused by the reduced etching potential of the acidic monomers toward the base of hybrid layers, or the presence of acidic but non-polymerisable hydrolytic adhesive components, creating potential sites for the degradation of the bonded created by these self-etch adhesives. (C) 2004 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available