Al and Zn samples were subjected to two-year influence of the microorganisms Penicillium frequentans, Aspergillus niger and Bacillus mycoides under laboratory conditions with controlled humidity (ca. 97%) and temperature (ca. 26 degreesC). These strains were isolated from Al, Cu, Zn and steel samples, which were exposed to marine, rural and urban sites in Lithuania. Electrochemical impedance spectroscopy (EIS) ascertained microbially influenced corrosion acceleration (MICA) of zinc samples. By contrast, microbially influenced corrosion inhibition was determined for aluminium samples. EIS data indicated a three-layer structure developed during zinc corrosion. The reasons of MICA lie mainly in diminishing of the inner layer (next to the metal), whose passivating capacity is much higher when compared to other layers. Two-layer structure was identified on aluminium samples: a native aluminium oxide and the layer resulted from oxide interaction with products of metabolism of microorganisms. A simultaneous increase in the oxide layer resistance and decrease in the layer thickness implied that microorganisms promoted passivity at the sites of localized corrosion (pores, micro-cracks, etc.). (C) 2005 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available