Ultra-high molecular weight polyhydroxyalkanoates (PHAs) with low polydispersity index (PDI = 1.3) were produced in a novel, pilot scale application of mixed cultures of nitrogen-fixing bacteria. The number average molecular weight (M (n)) of the poly(3-hydroxybutyrate) (P(3HB)) and poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (P(3HB-co-3HV)) was determined to be 2.4 x 10(6) and 2.5 x 10(6) g mol(-1), respectively. Using two types of carbon sources, biomass contents of the P(3HB) and P(3HB-co-3HV) were 18% and 30% (PHA in dry biomass), respectively. The extracted polymers were analysed for their physical properties using analytical techniques such as nuclear magnetic resonance (NMR) spectroscopy, differential scanning calorimetry (DSC) and gel permeation chromatography (GPC). NMR confirmed the formation of homopolymer and copolymer. DSC showed a single melting endotherm peak for both polymers, with enthalpies that indicated crystallinity indices of 44% and 37% for P(3HB) and P(3HB-co-3HV), respectively. GPC showed a sharp unimodal trace for both polymers, reflecting the homogeneity of the polymer chains. The work described here emphasises the potential of mixed colony nitrogen-fixing bacteria cultures for producing biodegradable polymers which have properties that are very similar to those from their pure-culture counterparts and therefore making a more economically viable route for obtaining biopolyesters.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available