A low cost chemical bath deposition (CBD) technique has been used for the preparation of Cu2-xSe thin films on glass substrates. Structural, electrical and optical properties of these films were investigated. X-ray diffraction (XRD) study of the Cu2-xSe films annealed at 523 K suggests a cubic structure with a lattice constant of 5.697 angstrom. Chemical composition was investigated by X-ray photoelectron spectroscopy (XPS). It reveals that absorbed oxygen in the film decreases remarkably on annealing above 423 K. The Cu/Se ratio was observed to be the same in as-deposited and annealed films. Both as-deposited and annealed films show very low resistivity in the range of (0.04-0.15) x 10(-5) Omega-m. Transmittance and Reflectance were found in the range of 5-50% and 2-20% respectively. Optical absorption of the films results from free carrier absorption in the near infrared region with absorption coefficient of similar to 10(8) m(-1). The band gap for direct transition, E-g.dir varies in the range of 2.0-2.3 eV and that for indirect transition E-g.indir is in the range of 1.25-1.5 eV. (C) 2005 Springer Science + Business Media, Inc.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available