Effect Of Y2O3-Al2O3 ratio on inter-granular phases and films in tape-casting α-SiC with high toughness

Silicon carbide (SiC) ceramics prepared from liquid phase sintering after aqueous-tape-casting can yield high toughness when appropriate amount Of Y2O3-Al2O3 are added, even though no elongated grains are present. Grain boundaries (GB), second-phases and hetero-phase boundaries (HB) in 2 samples with additive mole ratios of 3:5 and 3:7 are investigated using high-resolution and analytical electron microscopy (HREM and AEM). The meta-stable YAlO3 (YAP) was nucleated from SiC surfaces in the sample with Y/A1 = 3:5 as revealed by crystallographic relations across the HB, whilst relatively thick amorphous films were found at GB. In contrary, the higher level of Al2O3 additives decreases the GB film thickness in the sample with Y/Al = 3:7, and the homogeneous nucleation Of Y3Al5O12 (YAG) occurs at triple pockets accompanying with thick HB films. The strong variation of GB widths is a result of GB wetting in the sample with Y/Al = 3:5 and HB wetting in the sample of Y/Al = 3:7, both by liquid Al2O3. The energy of GB in the former sample is higher than the energy of HB as exhibited by the preferential nucleation of meta-stable YAP on SiC surfaces, which results in wetting of GB by the liquid; the situation is opposite in the latter sample as the wetting of HB occurs, leading to de-wetting of GB. The thermal mismatch between SiC and YAP or YAG as well as the presence of amorphous films facilitate the creation of micro-crack to promote inter-granular fracture and result in high toughness in both SiC ceramics. (c) 2005 Acta Materialia, Inc. Published by Elsevier Ltd. All rights reserved.