Journal
BIOMATERIALS
Volume 26, Issue 16, Pages 2847-2856Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.biomaterials.2004.08.015
Keywords
titanium; ion implantation; corrosion; biocompatibility
Ask authors/readers for more resources
This study is concerned with the effect of dual implantation of calcium and phosphorus upon the structure, corrosion resistance and biocompatibility of titanium. The ions were implanted in sequence, first Ca and then P, both at a dose of 10(17) ions/cm(2) at a beam energy of 25 keV. Transmission electron microscopy was used to investigate the microstructure of the implanted layer. The chemical composition of the implanted layer was examined by XPS and SIMS. The corrosion resistance was determined by electrochemical methods in a simulated body fluid (SBF) at a temperature of 37 degreesC. The biocompatibility tests were performed in vitro in a culture of human-derived bone cells (HDBC) in contact with the tested materials. The viability of the cells was determined by an XTT assay and their activity by the measurements of the alkaline phosphatase activity in contact with implanted and nonimplanted titanium samples. The in vitro examinations confirmed that, under the conditions prevailing during the experiments, the biocompatibility of Ca + P ion-implanted titanium was satisfactory. TEM results show that the surface layer formed by the Ca + P implantation is amorphous. The corrosion resistance of titanium, examined by the electrochemical methods, appeared to be increased after the Ca + P ion implantation. (C) 2004 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available