Journal
APPLIED CATALYSIS B-ENVIRONMENTAL
Volume 105, Issue 1-2, Pages 171-181Publisher
ELSEVIER
DOI: 10.1016/j.apcatb.2011.04.009
Keywords
Cellulose hydrolysis; Solid Lewis acid catalysts; Tungstated zirconia; Tungstated alumina; Lactic acid
Ask authors/readers for more resources
Crystalline cellulose treated in hydrothermal conditions (190 degrees C, 24h) is partially solubilised, 30%, into water soluble oligosaccharides/polymers with the formation of small amounts of glucose and 5-HMF. In the presence of solid Bronsted catalysts such as Cs2HPW12O40 and HY zeolite, the extent of the cellulose depolymerisation was not changed when no leaching occurred. However, a quite different products distribution was obtained, in favour of further transformations of glucose and HMF in levulinic and formic acids. On the opposite, solid Lewis acids such as tungstated zirconia (ZrW) and tungstated alumina (AIW) exhibited a remarkable promoting effect on the cellulose depolymerisation which was raised up to 45% while an unexpected decrease of the proportion of water soluble oligosaccharides/polymers was observed. Yields of 27 mol% and 18.5 mol% in lactic acid were achieved on AIW and ZrW, respectively. Moreover, these tungsten based Lewis acids exhibited a good stability and recyclability. The efficiency of the solid Lewis acids ZrW and AIW to produce lactic acid directly from crystalline cellulose was explained by a positive synergy between water autoprotolysis responsible of the cellulose depolymerisation into soluble intermediates which are further converted on the solid Lewis catalyst surface. (C) 2011 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available