Journal
APPLIED CATALYSIS B-ENVIRONMENTAL
Volume 90, Issue 3-4, Pages 405-415Publisher
ELSEVIER SCIENCE BV
DOI: 10.1016/j.apcatb.2009.03.031
Keywords
Ceria-zirconia solid solution; Nano; Supercritical water; Hydrothermal synthesis; Chemometric
Funding
- High-Throughput Nanoceramics Discovery project UAD, IR, JRGE, SY, TL [EP/D038499/1, EP/D038391/1]
- EPSRC [EP/17019823/1]
- EPSRC [EP/D038391/1, EP/F019823/1] Funding Source: UKRI
- Engineering and Physical Sciences Research Council [EP/F019823/1, EP/D038391/1] Funding Source: researchfish
Ask authors/readers for more resources
Two compositions Ce0.50Zr0.39La0.04Y0.07O2-delta and Ce0.25Zr0.65La0.04Y0.06O2-delta, based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000 degrees C, 1100 degrees C or 1200 degrees C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000 degrees C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity. (C) 2009 Elsevier B.V. All rights reserved.