Journal
IONICS
Volume 21, Issue 11, Pages 3031-3038Publisher
SPRINGER HEIDELBERG
DOI: 10.1007/s11581-015-1498-8
Keywords
Na plus conductors; Doping
Funding
- US Department of Energy's Office of Electricity Delivery and Energy Reliability
- Sandia National Laboratories [1161548]
Ask authors/readers for more resources
Doping the zirconium site in NASICON (Na3Zr2Si2PO12) with lower valent cations enhanced the ionic transport of the material. Both Na3.2Zr1.8M0.2Si2PO12 (M=Al3+, Fe3+, Y3+) and Na3.4Zr1.8M0.2Si2PO12 (M=Co2+, Ni2+, Zn2+) exhibited a higher bulk conductivity than undoped Na3Zr2Si2PO12 at room temperature. A decrease in the low temperature activation energy for all doped NASICON was observed, which helped contribute to the higher room temperature conductivity. The lower activation energy and enhanced conductivity of doped materials were a result of alterations in the NASICON structure. The charge imbalance created by aliovalent substitution increased the sodium in the lattice resulting in more charge carriers with better mobility. Furthermore, the conductivity was optimized by the ionic radius of the species in the zirconium site. Ultimately, NASICON doped with a +2 oxidation state cation having an ionic radius of approximately 0.73 (Zn and Co) attained a maximum in conductivity. Zn-doped NASICON displayed the greatest room temperature bulk conductivity of 3.75 Au 10(-3) S/cm, while Co-doped NASICON demonstrated the greatest total conductivity of 1.55 Au 10(-3) S/cm.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available