Synthesis of germanium nanocrystals in high temperature supercritical CO2

Germanium nanocrystals were synthesized in supercritical (SC) CO2 by thermolysis of diphenylgermane (DPG) or tetraethylgermane (TEG) with octanol as a capping ligand at 500 degrees C and 27.6 MPa. The Ge nanocrystals were characterized with high resolution transmission electron microscopy (HRTEM), energy-dispersive x-ray spectroscopy (EDS), and x-ray diffraction (XRD). On the basis of TEM, the mean diameters of the nanocrystals made from DPG and TEG were 10.1 and 5.6 nm, respectively. The synthesis in sc-CO2 produced much less organic contamination compared with similar reactions in organic supercritical fluids. When the same reaction of DPG with octanol was performed in the gas phase without CO2 present, bulk Ge crystals were formed instead of nanocrystals. Thus, the solvation of the hydrocarbon ligands by CO2 was sufficient to provide steric stabilization. The presence of steric stabilization in CO2 at a reduced temperature of 2.5, with a reduced solvent density of only 0.4, may be attributed to a reduction in the differences between ligand-ligand interactions and ligand-CO2 interactions relative to thermal energy.