Journal
BIOMATERIALS
Volume 26, Issue 24, Pages 5021-5031Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.biomaterials.2005.01.024
Keywords
collagen fibrils; dentin bonding; durability; AFM; SEM; TEM
Funding
- NIDCR NIH HHS [DE014911, DE015306] Funding Source: Medline
Ask authors/readers for more resources
This study investigates the effect of structural changes of collagen fibrils on the bonding durability of a total etch luting resin (Super-Bond C&B) and a self-etching luting resin (Panavia F 2.0) to dentin. An atomic force microscope (AFM) was used to observe structural changes of intact dentin collagen fibrils after acidic conditionings of two bonding systems. After 90d water storage and 15,000 thermal cycles (TC) as artificial aging, micro-tensile bond strength (mu TBS) was utilized to evaluate the bonding durability of the two bonding systems to dentin. mu TBS after 1d or 90d water storage without TC were separately measured in control groups. A cross-banding periodicity of about 67 nm along collagen fibrils was seen on demineralized intertubular dentin surfaces in AFM images. For both luting resins, thermal cycling decreased (p < 0.05) pTBS of 1d and 90d, compared to controls. Scanning electron microscope and transmission electron microscopic examinations revealed that the top and bottom of hybrid layer (HL) were weak links in the bonding interface over time. The results Suggest that the top of HL contains disorganized collagen fibrils from the smear layer which degrade over time. AFM results indicate that the demineralized intact collagen fibrils beneath the smear layer were not denatured during acidic conditioning. However, these collagen fibrils may be structurally unstable due to poor infiltration by resin or loss of resin protection within the HL over time, reducing the long-term pTBS. This process was accelerated by thermal fatigue cycling. (c) 2005 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available