Journal
SURFACE & COATINGS TECHNOLOGY
Volume 200, Issue 5-6, Pages 1913-1919Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2005.08.021
Keywords
titanium oxide; anodizing; impedance spectroscopy; laser; ion implantation; surface micropatterning
Ask authors/readers for more resources
Ceramic oxide films like TiO2 are used on medical implants to improve biocompatibility and corrosion behavior. Along with the chemical composition, the topography of implants with surface features in the tens of microns range is known to promote osteointegration. In this work, the prospective of anodically gown TiO2 thin films as mask material for subsequent electrochemical micro/nanopatterning of medical implant surfaces sensitized by He-ion beam and YAG-laser irradiation is investigated. Electrochemical impedance spectroscopy was used to characterize resistance and capacitance of oxide films anodized under various conditions. The resistance obtained by fitting to an appropriate equivalent circuit was compared to the film stability in electrochemical pitting experiments. Film thickness, composition and microstructure were analyzed by glow discharge optical emission spectroscopy (GDOES), Xray photoelectron spectroscopy, scanning and transmission electron microscopy and Raman spectroscopy. An increasing film resistance of the porous part of the oxide was found to correlate to increasing pitting resistance. GDOES revealed a low carbon and sulfur concentration in the film as well as an accumulation of hydrogen at the oxide/metal interface. Based on the performance in pitting tests, suitable anatase TiO2 films were used for laser micropatterning, and thinner mainly amorphous films were used for He-ion beam micropatterning experiments. YAG-laser treatment led to preferential dissolution of the irradiated sites during the subsequent etching step. Both preferential and reduced dissolution was observed in case of He-ion implantation. Potential physico-chemical mechanisms for observed micropatteming effects are discussed. (c) 2005 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available