POLYMER
Volume 46, Issue 25, Pages 11624-11634Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.polymer.2005.09.076
Keywords
polymer nanocomposites; microstructure; clay dispersion
Categories
Ask authors/readers for more resources
Polypropylene (PP)/clay nanocomposites prepared by melt blending using different clays and coupling agents based on maleic anhydride-grafted PP (MA-PP) were studied. Clay dispersion using field emission gun scanning electron microscope (FEG-SEM) and transmission electron microscopy (TEM), and PP matrix morphology were characterized. Clay dispersion was improved in the presence of MA-PP, as shown by the higher particles Surface density (number of particles/mm(2)) at all micro-, sub-micro- and nano-levels. The PP spherulite diameter was affected by both the presence of MA-PP and clay dispersion. Clay intercalation, characterized by both complementary X-ray diffraction (XRD) and TEM, was greatly influenced by the characteristics of MA-PP. The use of low molecular weight (M-w) MA-PP led to a good and uniform intercalation but with no further possibility to exfoliation. The use of higher M-w MA-PP led to a heterogeneous intercalation with signs of exfoliation. The crystallization behavior of nanocomposites was studied by differential scanning calorimetry (DSC). When fine clay dispersion was achieved with MA-PP, clay-nucleating effect was limited and lower crystallization temperature and rates were observed. It was also shown by wide angle X-ray diffraction (WAXD) that clay induced some orientation of alpha-phase PP crystallites. (c) 2005 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available