JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS
Volume 44, Issue 2, Pages 312-325Publisher
WILEY
DOI: 10.1002/polb.20697
Keywords
aging; degradation; intercalation; montmorillonite; nanocomposite; plasticization; polylactide; thermal behavior; viscoelastic properties
Categories
Ask authors/readers for more resources
Plasticized polylactide (PLA) - layered silicate nanocomposites were obtained by melt blending PLA with polyethylene glycol as plasticizer (20 wt %) and with different montmorillonite fillers: Cloisite (R) 20A, Cloisite (R) 25A, and Cloisite (R) 30B (from 1 to 10 wt %). Comparative samples of melt-blended polylactide (without filler) and plasticized PLA with 20 wt % PEG were considered as well. Samples have been aged for 1 and 4 years and their chemical and physical characteristics were compared with not aged reference ones. It was found that molecular weight of the PLA decreased upon melt-processing and aging, particularly when the Cloisite content increased, without a clear relation to the nature of the organo-modifier. On the contrary, the PEG plasticizer was practically undegraded upon melt processing and aging. Structural studies revealed that plasticized PLA and plasticized PLA-based nanocomposites are unstable in time of aging and undergo deplasticization. They showed, after aging, the presence of a thin PEG crystalline layer at the surface of the samples and improved the order in the PLA matrix to a higher extent in plasticized polylactide than in plasticized nanocomposite (due to clay stabilization effect). The amount of PEG diffusing toward sample surface was correlated with aging time, molecular weight of PLA matrix, and Cloisite (R) type, in clear relation to the extent of intercalation with PLA and PEG. Some modifications of the viscoelastic properties of PLA matrix, induced by the presence of both the nanoparticlate filler and the plasticizer, as well as a deterioration of the mechanical properties upon aging were observed. (c) 2005 Wiley Periodicals, Inc.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available