Improved thermoelectric properties of gadolinium intercalated compounds GdxTiS2 at the temperatures from 5 to 310 K

The thermoelectric properties of Gd intercalated Compounds GdxTiS2 have been investigated at the temperatures from 5 to 310 K. The results indicate that Gd intercalation into TiS2 leads to substantial decrease of both its electrical resistivity and its lattice thermal conductivity K-L (K-L is lowered by 20% and 46% at 300 K for x = 0.025 and 0.05, respectively). Specially, as compared to the pristine TiS2 the figure of merit ZT of the intercalated Compound GdxTiS2 has been improved at all temperatures investigated, and specifically, the ZT value of Gd0.05TiS2 at 300 K is about three times as large as that of TiS2.