Journal
APPLIED SURFACE SCIENCE
Volume 252, Issue 10, Pages 3812-3817Publisher
ELSEVIER
DOI: 10.1016/j.apsusc.2005.05.076
Keywords
nanocomposites; electroplating; coatings; hall-patch; Orowan
Ask authors/readers for more resources
ZrO2 nanoparticles was uniformly co-deposited into a nickel matrix by electroplating of nickel from a Watts bath containing particles in suspension which were monodispersed with dispersant under DC electrodeposition condition. It was found that morphology, orientation and hardness of the nanocomposite coatings with monodispersed ZrO2 nanoparticles had lots of difference from the nanocomposite coatings with agglomerated ZrO2 nanoparticles and pure nickel coatings. Especially, the result of hardness showed that only a very low volume percent (less than 1 wt.%) of monodispered ZrO2 nanoparticles in Ni-ZrO2 nanocomposite coatings would result in higher hardness of the coatings. The hardness of Ni-ZrO2 nanocomposite coatings with monodispersed and agglornerated ZrO2 nanoparticles were 529 and 393 HV, respectively. The hardness value of the former composite coatings was over 1.3 times higher than that of the later. All these composite coatings were two-three times higher than that of pure nickel plating (207 HV) prepared under the same condition. The strengthening mechanisms of the Ni-ZrO2 nanocomposite coatings based on a combination of grain refinement strengthening from nickel matrix grain refining and dispersion strengthening from dispersion state of ZrO2 nanoparticles in the coatings. (c) 2005 Published by Elsevier B.V.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available