Porous scaffolds composed of collagen or collagen and elastin were prepared by freeze drying at temperatures between -18 and -196 degrees C. All scaffolds had a porosity of 90-98% and a homogeneous distribution of pores. Freeze drying at -18 degrees C afforded collagen and collagen/elastin matrices with average pore sizes of 340 and 130 mu m, respectively. After 20 successive cycles up to 10% of strain, collagen/elastin dense films had a total degree of strain recovery of 70% +/- 5%, which was higher than that of collagen films (42% +/- 6%). Crosslinking of collagen/elastin matrices either in water or ethanot/water (40% v/v) was carried out using a carbodiimide (N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride, EDC) in combination with a succinimide (N-hydroxysuccinimide, NHS) in the presence or absence of a diamine (J230) or by reaction with butanediol diglycidylether (BDGE), followed by EDC/NHS. Crosslinking with EDC/NHS or EDC/NHS/J230 resulted in matrices with increased stiffness as compared to noncrosslinked matrices, whereas sequential crosslinking with the diglycidylether and EDC/NHS yielded very brittle scaffolds. Ethanou water was the preferred solvent in the crosslinking process because of its ability to preserve the open porous structure during crosslinking. Smooth muscle cells were seeded on the (crosslinked) scaffolds and could be expanded during 14 days of culturing. (c) 2005 Wiley Periodicals, Inc.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available