The authors studied the effect of vanadium addition on the microstructure and properties of Al0.5CoCrCuFeNi high-entropy alloy. The microstructure of Al0.5CoCrCuFeNiVx (x = 0 to 2.0 in molar ratio) alloys was investigated by scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction. With little vanadium addition, the alloys are composed of a simple fee solid-solution structure. As the vanadium content reaches 0.4, a BCC structure appears with spinodal decomposition and envelops the FCC dendrites. From x = 0.4 to 1.0, the volume fraction of bee structure phase increases with the vanadium content increase. When x = 1.0, fee dendrites become completely replaced by bee dendrites. Needle-like sigma-phase forms in bee spinodal structure and increases from x = 0.6 to 1.0 but disappears from x = 1.2 to 2.0. The hardness and wear resistance of the alloys were measured and explained with the evolution of the microstructure. The hardness values of the alloys increase when the vanadium content increases from 0.4 to 1.0 and peak (640 HV) at a vanadium content of 1.0. The wear resistance increases by around 20 pet as the content of vanadium increases from x = 0.6 to 1.2 and levels off beyond x = 1.2. The optimal vanadium addition is between x = 1.0 and 1.2. Compared with the previous investigation of Al0.5CoCrCuFeNi alloy, the vanadium addition to the alloy promotes the alloy properties.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available