WEAR
Volume 260, Issue 11-12, Pages 1166-1172Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.wear.2005.07.006
Keywords
plasma spraying; ceramic coating; lamellar bonding; particle erosion; debonding mechanism; alumina
Ask authors/readers for more resources
The lamellar structure determines mechanical properties of a thermal spray coating. A model for the erosion of thermally sprayed ceramic coatings resulting from the debonding of flattened ceramic particles is proposed based on the examination of the erosion mechanism. The relationship between erosion rate and microstructural parameters is established both experimentally and theoretically to reveal main lamellar structural parameters controlling erosion of thermally sprayed ceramic coating. The microstructural parameters include the mean bonding ratio between lamellae and thickness of the lamellae. The erosion rate of plasma-sprayed Al2O3 coatings was measured at impact angle of 90 degrees under the fixed erosion test conditions. The correlation of theoretical model with the observed structural parameters and erosion data of alumina coatings was examined. It is revealed that the theoretical relationship agreed well with the observed relation. The results clearly revealed that the erosion of plasma-sprayed ceramic coating was inversely proportional to the mean lamellar bonding ratio. The influences of spray parameters on erosion effected mainly through their influences on the lamellar bonding. The erosion resistance of a thermally sprayed ceramic coating was controlled by coating fracture toughness. (c) 2005 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available