Studies on the morphologies of LiCoO2 films prepared by soft solution processing

Lithium cobalt oxide films were prepared on nickel plates and foam nickel by soft solution processing method. The films were characterized by chemical analysis, X-ray diffraction, scanning electron microscopy, and atomic force microscopy. It was found that growth of LiCoO2 crystal on polished nickel plates and foam nickel led to different morphologies of LiCoO2. A compact LiCoO2 film was formed on smooth nickel plates while some grassy LiCoO2 crystals formed and scattered on the surface of foam nickel, which indicates different mechanism of films growth. Formation of LiCoO2 crystal on nickel plates shows the characteristic of two-dimensional nucleation while on foam nickel shows the characteristic of preferential nucleation. Further, increase of LiOH concentration in the soft solution results in morphological change of LiCoO2 film from hexagonal platelets to spherical grains. In addition, the larger the current density, the less the grain size and the porosity inside grains are. (c) 2006 Elsevier B.V. All rights reserved.