Journal
JOURNAL OF APPLIED POLYMER SCIENCE
Volume 101, Issue 3, Pages 1763-1774Publisher
WILEY-BLACKWELL
DOI: 10.1002/app.23516
Keywords
carbon black filled powdered rubber; natural rubber; particle size distribution; powdering mechanism; mechanical properties; SEM analysis
Categories
Ask authors/readers for more resources
Carbon black (HAF) filled powdered natural rubber (P(NR/HAF)) was prepared and the particle size distribution, mechanical properties, and micromorphology of P(NR/HAF) were studied. A carbon black-rubber latex coagulation method was developed for preparing carbon black filled free-flowing, noncontact staining NR powders with particle diameter less than 0.9 mm. A powdering mechanism model was put forward to describe the powdering process, which shows that the key technical points consist in the surfactant with good emulsification properties and the polymer coating resin with good film forming properties. SEM analysis shows that carbon black and rubber matrix have formed a macroscopic homogenization in the P(NR/ HAF) particles without contact staining, and carbon black particles are well dispersed in rubber matrix with diameter of about 50-150 nm. P(NR/HAF) vulcanizate showed better mechanical properties than bale natural rubber/carbon black blends (NR/HAF) and simple NR latex/carbon black blends (NRL/HAF), which depends primarily upon the absence of free carbon black, the fine dispersion of filler on the rubber matrix, and the better interaction between carbon black and rubber matrix due to the proper preparation condition of noncontact staining carbon black filled powdered NR. (c) 2006 Wiley Periodicals, Inc.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available