Synthetic bioactive materials offer possibilities to repair large tissue defects. It is well known that bioactivity, angiogenesis, and inflammation are key events in implant incorporation. Using glass-coated and glass-free collagen as potential bone graft substitutes, we carried out in vitro bioactivity and an in vivo angiogenesis and inflammation studies. The in vitro study showed bioactivity when the glass-coated samples were left in SBF for 5 days. This was confirmed by FTIR results, which presented P-O vibration bands characteristic of hydroxyapatite close to 1060 cm(-1) and 600 cm(-1). The in vivo response was evaluated following subcutaneous implantation of the biomaterial in the mouse dorsa. Angiogenesis, as determined by hemoglobin content extracted from implants 7 and 14 days after implantation, increased progressively in both glass-coated and glass-free collagen implants. However, vascularization was higher in the glass-coated collagen implants 14 days after implantation (mu g Hb per mg wet tissue 6.0 +/- 0.3) compared with the glass-free group (1.6 +/- 0.1). The inflammatory process, determined by the levels of myeloperoxidase and N-acetylglucosaminidase, was similar for both implants. This study shows that glass-coated collagen implants hold osteogenic and angiogenic potential and may be used in clinical conditions requiring improvement of these biological processes. (c) 2006 Wiley Periodicals, Inc.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available