Synthesis and characterization of waterborne polyurethane adhesives containing different amount of ionic groups (I)

A series of waterborne polyurethanes (WBPU) containing different amount of 2,2-bis(hydroxymethyl) propionic acid (DMPA) were synthesized using prepolymer mixing process. Relationships between the DMPA content and physical, mechanical, and thermal properties as well as adhesive behavior at different condition were investigated. Stable aqueous dispersions of WBPU were obtained when the DMPA content was more than 10 mol %. At higher DMPA content, the particle size of the WBPU dispersion was lower but the viscosity of the dispersion was higher. Water swelling and tensile strength of the films increased with increasing of DMPA content. The optimum adhesive strength of WBPU adhesives was found to be depended on the DMPA content, pressing temperature, and pressure on adhesion process. The adhesive strength of WBPU adhesives increased with increasing DMPA content. The optimum pressing temperature decreased with increasing DMPA content. The adhesive strength of WBPU adhesives increased with increasing pressure up to 15 kg f/cm(2) and then leveled off. The optimum pressing temperature of WBPU adhesives samples containing 24.02, 22.05, and 17.05 mol % DMPA was about 100, 120, and 140 degrees C, respectively. (c) 2006 Wiley Periodicals, Inc.