Preparation of hydroxyapatite/zirconia bioceramic nanocomposites for orthopaedic and dental prosthesis applications

Homogeneous mixtures of hydroxyapatite (HAp) and yttria-stabilized zirconia (YSZ) nanoparticles were successfully synthesized using chemical co-precipitation and subsequent calcination. For the synthesis of HAp/YSZ nanopowder, the Ca/P atomic ratio was 1.73 to obtain high-content stoichiometric hydroxyapatite phase and to suppress beta-tricalcium phosphate (beta-TCP) formation. The agglomerated crystalline powders were milled using YSZ ball media to obtain well-separated nanoparticles. The final particle size of the HAp and YSZ was similar to 50-70 and similar to 15-30 nm, respectively. The crystallinity and morphological feature of the nanopowder was analysed using x-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM) analyses. The ball-milled nanopowder mixture was hot pressed at 1100 degrees C for 1 h under 20 MPa in vacuum atmosphere. The sintered HAp/YSZ nanocomposites exhibited approximately 99% of the theoretical density, due not only to the fine nanoscale of the particles, but also to the homogeneous distribution of the nanoparticle mixture. They also showed fine grain structures of the HAp phase due to the suppressed grain growth by YSZ particles. The nanocomposites showed improved mechanical properties, flexural strength of similar to 155 MPa and fracture toughness of similar to 2.1 MP m(1/2), due to the YSZ contribution to the HAp matrix.