Thermal behavior of polyacrylonitrile polymers synthesized under different conditions and comonomer compositions

Polyacrylonitrile (PAN) polymers are used as precursors for carbon fiber production. This process requires an oxidative stabilization step, which can be studied by differential scanning calorimetry (DSC). In this sense, thermal behavior of PAN based terpolymers by different polymerization processes, compositions and itaconic acid concentrations in the reaction media were investigated. The obtained results showed that the addition of itaconic acid and methyl acrylate as comonomers resulted a lower heat flow during the process comparing to the PAN homopolymer. It suggested that these comonomers aid the oxidative stabilization stage for all studied process. The redox system polymerization at 40 degrees C resulted in a lower heat flow. Itaconic acid decreases slightly initial and peak temperatures of the terpolymer and heat flow until concentration of 3y. The cyclization temperature decreases when MAis incorporated into the terpolymer compared to the MMA terpolymer and increases when MAA is the acidic monomer. Among terpolymers the AN/MA/AA polymer showed the best thermal behavior for carbon fiber producing.