COLLOIDS AND SURFACES B-BIOINTERFACES
Volume 55, Issue 1, Pages 51-58Publisher
ELSEVIER SCIENCE BV
DOI: 10.1016/j.colsurfb.2006.11.007
Keywords
surfactant; thermosensitive magnetic nanoparticles; N-isopropylacrylamide; superparamagnetism
Ask authors/readers for more resources
Thermosensitive polymer coated nanomagnetic adsorbents were synthesized by seed polymerization using surface modified nanomagnetic particles as the seeds. The Fe3O4 nanomagnetic particles were prepared by chemical precipitation of Fe2+ and Fe3+ salts in the ratio of 1:2 under alkaline and inert condition. The surface of these particles was modified by surfactants to achieve stability against agglomeration. These stable particles were then polymerized using N-isopropylacrylamide (NIPAM) as the main monomer, methylene-bis-acrylamide as the crosslinker and potassium per sulfate as the initiator. The thermosensitive adsorbents were characterized by using transmission electron micrography (TEM) and vibrating sample magnetometer (VSM). TEM showed that the particle remained discrete with a mean diameter of 12 nm. Magnetic measurements revealed that the particles are superparamagnetic out), with a decrease of magnetism after binding with the polymer due to the increase in surface spin disorientation. Pure Fe3O4 spinel structure of these nanoparticles was indicated by the X-ray diffraction (XRD) patterns. The polymerization of NIPAM with the surface modified nanomagnetic particles was confirmed by Fourier transform spectroscopy (FTIR), Thermogravimetric analysis (TGA) and X-ray photoelectron spectroscopy (XPS). In addition, the adsorption/desorption of BSA molecule on these thermosensitive nanoparticles was investigated as a function of temperature. More than 60% desorption efficiency was achieved under appropriate condition. (C) 2006 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available