JOURNAL OF POROUS MATERIALS
Volume 14, Issue 2, Pages 165-171Publisher
SPRINGER
DOI: 10.1007/s10934-006-9021-2
Keywords
aerogels; hydrophobicity; contact angle; transmission electron microscopy (TEM); infrared spectroscopy (IR)
Ask authors/readers for more resources
The experimental results on the surface modification of tetraethoxysilane (TEOS) based silica aerogels using trimethylethoxysilane (TMES) as a co-precursor by two step sol-gel process are reported. The molar ratio of MeOH/TEOS was fixed at 17 and TMES/TEOS ratio was varied from 0.38 to 1.14. The concentration and quantity of acidic water (oxalic acid) added in the first step and base water (ammonium hydroxide) in the second step were also varied. The best quality superhydrophobic aerogels could be obtained with only distilled water (without any acid catalyst) in the first stage and the basic water in the second step of the sol-gel process. The molar ratio of TEOS: TMES: MeOH: distilled water: basic water was optimized at 1:0.86:17:4.9:4.9, respectively. The surface modification has been confirmed from the Fourier transform infrared spectroscopy measurements while the hydrophobicity was quantified in terms of the contact angle measurements. The TMES/TEOS based aerogel powder could be used to transport micro-liters of water in the form of water marbles. The aerogels have been characterized by the bulk density, porosity, thermal conductivity, contact angle measurements and the transmission electron microscopy (TEM).
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available