SUPERLATTICES AND MICROSTRUCTURES
Volume 42, Issue 1-6, Pages 231-235Publisher
ACADEMIC PRESS LTD- ELSEVIER SCIENCE LTD
DOI: 10.1016/j.spmi.2007.04.022
Keywords
diluted magnetic semiconductors; ZnO; magnetoresistance
Categories
Ask authors/readers for more resources
Due to the small magnetic moments observed for 3d transition metals in ZnO [M. Diaconu, H. Schmidt, H. Hochmuth, M. Lorenz, G. Benndorf, J. Lenzner, D. Spernann, A. Setzer, K.W Nielsen, P. Esquinazi, M. Grundmann, Thin Solid Films 486 (2005) 117], there is still space for optimizing ZnO-based diluted magnetic semiconductors for spintronics applications. Motivated by the observation of magnetic moments as high as 4000 mu(B)/Gd atom in GaN:Gd [S. Dhar, O. Brandt, M. Ramsteiner, V.F. Sapega, K.H. Ploog, Phys. Rev. Lett. 96 (2005) 037205], we investigated ZnO films doped with 0.01, 0.1 or I at.% rare earth (RE) metals. The films, with thicknesses between 20 nm and 1 mu m, have been grown by pulsed laser deposition on a-plane sapphire or fused silica substrates. The homogenous incorporation of the RE ions in ZnO was investigated by combined Rutherford backscattering and particle induced X-ray emission measurements. Hall measurements revealed an unexpected dependence of the electron concentration on film thickness, proving a non-uniform distribution of electrically active defects. Magnetotransport measurements at different temperatures were performed to study the magnetoresistance and the presence of the anomalous Hall effect. Large negative magnetoresistance was obtained at 5 K, while no anomalous Hall effect was observed. These results indicate that there are no exchange interactions between the RE ions. (c) 2007 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available