INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
Volume 32, Issue 13, Pages 2504-2512Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.ijhydene.2006.11.012
Keywords
hydrogen storage; carbon nanohorn; activated carbon; carbon nanotubes; graphitic carbon nanofiber
Categories
Ask authors/readers for more resources
Hydrogen storage capacity of various carbon materials, including activated carbon (AC), single-walled carbon nanohorn, single-walled carbon nanotubes, and graphitic carbon nanofibers, was investigated at 303 and 77 K, respectively. The results showed that hydrogen storage capacity of carbon materials was less than 1 wt% at 303 K, and a super activated carbon, Maxsorb, had the highest capacity (0.67 wt%). By lowering adsorption temperature to 77 K, hydrogen storage capacity of carbon materials increased significantly and Maxsorb could store a large amount of hydrogen (5.7 wt%) at a relatively low pressure of 3 MPa. Hydrogen storage capacity of carbon materials was proportional to their specific surface area and the volume of micropores, and the narrow micropores was preferred to adsorption of hydrogen, indicating that all carbon materials adsorbed hydrogen gas through physical adsorption on the surface. (C) 2006 International Association for Hydrogen Energy. Published by Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available