Journal
RADIATION PHYSICS AND CHEMISTRY
Volume 76, Issue 11-12, Pages 1741-1745Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.radphyschem.2007.02.086
Keywords
ultra-fine powdered styrene-butadiene rubber; radiation grafting; maleic acid; maleic anhydride
Ask authors/readers for more resources
The functionalization of ultra-fine powdered styrene-butadiene rubber (UFSBR) was carried out using gamma radiation-induced graft polymerization of maleic acid (MA) and maleic anhydride (MAH), respectively. It was found that the graft yield of MA onto UFSBR increased rapidly up to the peak and then decreased with increasing MA content. Moreover, the peak shifted to the direction of lower MA content with increasing absorbed dose. Similarly, there was the peak of graft yield with increasing MAH content for grafting of MAH onto UFSBR, whereas the peak of graft yield was achieved at 10wt% MAH content at different absorbed doses. On the other hand, increasing absorbed dose and decreasing monomer contents are useful to improve the graft efficiency of MA and MAH. At high dose and low monomer content, the graft yield of MAH onto UFSBR is higher than that of MA. FTIR spectra confirmed that both MA and MAH can be grafted successfully onto the UFSBR under gamma irradiation, respectively. Comparing with maleation of rubber by melt grafting, the graft yield of MAH on UFSBR is higher, which can be attributed to the network structure and nanometer size of UFSBR as well as high energy provided by radiation. (C) 2007 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available