JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY
Volume 45, Issue 23, Pages 5387-5397Publisher
WILEY
DOI: 10.1002/pola.22283
Keywords
crystallization; differential scanning calorimetry (DSC); living radical polymerization; miktoarm stars; polarized optical microscopy; ring-opening polymerization; TEM
Categories
Ask authors/readers for more resources
An heterofunctional initiator combining two reactive sites for ring opening polymerization and two for atom transfer radical polymerization was used to prepare three A(2)B(2) miktoarm star copolymers of poly(e-caprolactone) (PCL) and polystyrene (PS). The morphology and thermal properties were studied by transmission electron microscopy, polarized light optical microscopy, and differential scanning calorimetry. The (PCL)(2)(PS)(2) 72/28 (72 wt % PCL) sample was crystallized from a disordered melt. In this case, crystallization drove the structure formation and a lamellar morphology was obtained at the microdomain level, while spherulites were observed at a superstructural level. The other two samples, 39/61 and 27/73, with lower PCL content and higher total molecular weight, were not able to form spherulites. Surprisingly, these miktoarm star copolymers exhibited hexagonally packed cylinders and spheres morphologies, respectively, instead of lamellar and cylindrical morphology. Such unexpected and novel behavior was explained in terms of the higher resistance of the arms to be stretched in a miktoarm star copolymer when compared with the corresponding linear diblocks. (c) 2007 Wiley Periodicals, Inc.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available