Evaluation of improvement of physical and mechanical properties of bamboo fibers due to alkali treatment

Bamboo strips treated with caustic solutions of different concentrations, e.g., 5%, 10%, 15%, 20%, 25%, and 50%, were subjected to mechanical testing giving stresses on tensile strength, percent elongation at break, flexural strength, flexural modulus, and toughness. The change in average density was -15%, and the weight loss value shows a maximum of 21.94% at 50% alkali treatment. The mechanical properties of bamboo strips increase steadily with increasing concentration of caustic soda, showing a comparable increased value at 15 and 20%, and then exhibiting a gradual fall. The percent elongation at break corroborates these observations showing a continuous decreasing trend. The properties under investigation exhibit a clear transition in between 15 and 20% alkali concentration. The morphology of strips was studied by scanning electron microscope and polarizing light microscope. The crystal structure of both untreated and treated strips was compared by XRD analysis. In both cases, the breakdown of the crystal structures of the cellulose fibers and the recrystallization or reorientation of the degraded chains that are devoid of hemicellulose are quite apparent. However, at a very high concentration (to the extent of 25%) the breakdown of structure predominates much more over the reorientation or recrystallization. (C) 2007 Wiley Periodicals, Inc.