Soft-templating synthesis and adsorption properties of mesoporous carbons with embedded silver nanoparticles

Mesoporous carbons containing silver nanoparticles have been successfully synthesized under acidic conditions by employing resorcinol and formaldehyde as carbon precursors and triblock copolymer EO(101)PO(56)EO(101) (Lutrol F127) as a soft template. Silver nanoparticles of similar to 90 nm were added to the synthesis mixture to achieve 10 wt% and 20 wt% of Ag loading in the carbon. Also, tetraethyl orthosilicate (TEOS) was introduced to the system in order to improve adsorption properties of the silver-carbon composites and to reinforce its structure. The resulting carbons with incorporated silver nanoparticles featured high surface areas, large total pore volumes and primary mesopores in the range between similar to 6-7 nm.