Journal
ADSORPTION SCIENCE & TECHNOLOGY
Volume 32, Issue 6, Pages 465-474Publisher
MULTI-SCIENCE PUBL CO LTD
DOI: 10.1260/0263-6174.32.6.465
Keywords
-
Funding
- Department of Science and Technology (DST), New Delhi, India
Ask authors/readers for more resources
Nanocrystalline vanadium nitride (VN) materials are synthesized by two different routes, namely, the urea route and the ammonia route, using various V2O5 precursors obtained by citric acid based sol gel method. The VN nanomaterials obtained are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and BET method. The XRD patterns show the presence of pure cubic phase with line broadening. The lattice parameters were found to be 4.1266 and 4.1136 angstrom for the urea route and 4.1125 and 4.1120 angstrom for the ammonia route using V2O5 precursors heat treated at 350 and 550 degrees C, respectively. The estimated crystallite sizes are found to be 9 and 7 nm for the urea route and 22 and 28 nm for the ammonia route using V2O5 precursors synthesized at 350 and 550 degrees C, respectively. The SEM images show the presence of agglomerates having particle dimensions of 115 and (300 x 15) nm for the urea route and 111 and 68 nm for the ammonia route using V2O5 precursors heat treated at 350 and 550 degrees C, respectively. The maximum BET surface area of 57 m(2)/g was obtained for VN sample synthesized by the urea route using V2O5 precursors synthesized at 350 degrees C. The isotherms show typical Type IV with H2 hysteresis, which is characteristic of the mesoporous particles. The production of high-surface-area nitride materials has been correlated to synthetic procedure, precursor used and formation of mesopores in the material.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available