Micro and Nano-Texturization of Intermetallic Oxide Alloys by a Single Anodization Step: Preparation of Artificial Self-Cleaning Surfaces

Micro- and nanostructures of Ti-gamma Cu (gamma = 0, 30, 50, 70, and 100 wt %) intermetallic alloys were produced through a single anodization step. It was found that the original alloy composition influences the final oxide morphology obtained after anodization which presented formation of a microstructure with nanotubes, nanoparticles or nanopillars on the surface. Pure Ti and Cu oxide metals and their alloys presented hydrophilic or superhydrophilic properties immediately after anodization. When the anodized pure metal and/or Ti-gamma Cu surfaces were functionalized with trimethoxypropylsilane (TPMSi), by dipping and coating with a thin perfluorinated layer, the treated substrates became in all cases superhydrophobic (water contact angles in the range of 152-166 degrees), showing excellent self-cleaning properties with hysteresis below 3 degrees. These results can be explained by a combination of nanomicro morphologies with low surface energy compounds in the topmost monolayers. The decrease in hysteresis was associated with a higher M-OH bond concentration on the anodized surfaces, which allowed For more complete TMPSi coating coverage. This study also indicates that easy and effective fabrication of superhydrophobic surfaces in pure metals and alloys is possible without involving traditional multistep processes.