Journal
ACS APPLIED MATERIALS & INTERFACES
Volume 1, Issue 8, Pages 1813-1820Publisher
AMER CHEMICAL SOC
DOI: 10.1021/am900356e
Keywords
carbonate hydroxyapatite; films; pulsed laser deposition; characterization; hardness
Ask authors/readers for more resources
Carbonated hydroxyapatite (CHA)-coated titanium can Find wide applications as bone substitute implant in bone and dental surgery and orthopedics, promoting osseointegration with a host bone and ensuring biocompatibility and bioactivity. In this work, carbonated hydroxyapatite films were prepared on titanium substrates by pulsed laser deposition at different substrate temperatures ranging from 30 to 750 degrees C. The properties OF films were investigated by scanning electron microscopy, atomic force microscopy, energy-dispersive X-ray diffraction, and Fourier transform infrared spectroscopy. Vickers microhardness measurements of the composite film-substrate systems were performed, and the intrinsic hardness of films was separated from the composite hardness using a law-of-mixtures approach and taking into account the indentation size effect. The prepared CHA films are nearly stoichiometric with a Ca/P atomic ratio OF 2.0-2.2. The films deposited in the 30-500 degrees C temperature range are about 9 mu m thick, amorphous, having an average roughness of 60 nm. At higher temperature, 700-750 degrees C, the films are about 4 mu m thick, show a finer surface morphology and an average roughness of 20 nm. At 750 degrees C the films are amorphous, whereas at 700 degrees C they are crystalline and textured along the (202) and (212) directions. The intrinsic hardness of the films increased with an increase in substrate temperature, being as low as 5 GPa at 30 degrees C and reaching a high value of 28 GPa at 700 degrees C. The rich information gained by the joint use of the mentioned techniques allowed a comprehensive characterization of this system.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available