Conjugated polymers such as poly(3-hexylthiophene) (P3HT) are commonly used as semiconducting components in organic photovoltaics (OPVs) and organic thin-film transistors (OTFTs). Such devices may be exposed to oxygen or moisture in air and increased temperature during operation, potentially affecting their charge transport properties. Therefore, we produced the first reported examples of OTFTs using PBDB-T, a conjugated push-pull polymer used in high performance OPVs, and assessed their performance compared to P3HT under different environmental conditions. Drop casted and annealed bottom-gate, bottom-contact (BGBC) devices had an average mobility of 0.06 cm(2) V-1 s(-1), an on/off current ratio of 104 and a desirable threshold voltage around 0 V. These OTFTs showed distinct responses to characterization at increased temperature in vacuum (P < 0.1 Pa) and air, with PBDB-T devices retaining their performance better than P3HT over time. These findings suggest PBDB-T has higher stability to oxidation when exposed to air than P3HT, especially at high temperatures, and therefore represent a more stable alternative for use in OTFTs and OPVs.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available