Fabrication of a high sensitivity and fast response self-powered photosensor based on a core-shell silicon nanowire homojunction

Core-shell self-powered SiNWs homojunction photosensors have been fabricated. SiNWs are prepared by a metal assisted chemical etching method using different HF/H2O2 ratios and etching times. The length of the p-SiNWs increased as the H2O2 concentration and etching time increased. All the grown SiNWs show very low (similar to 0.7%) optical reflectance for the wavelength range of 200-1100 nm. Photoluminescence spectra of all prepared SiNWs show sharp and broad emission bands located in the red region of the light spectrum. Core-shell homojunction photosensors were fabricated by spin coating P2O2 onto the surface of the prepared p-SiNWs and annealed at 900 degrees C for 1 h. The fabricated devices exhibited photovoltaic behavior and high photosensitivity with fast response speed to the visible light. However, the sample that was fabricated using HF/H2O2 ratio of 1:1 showed the highest photosensitivity value of 3578% while the photosensor prepared using 2:1 ratio of HF/H2O2 gave the faster rise and decay time. (C) 2018 Elsevier Ltd. All rights reserved.