Journal
RUSSIAN JOURNAL OF PHYSICAL CHEMISTRY A
Volume 92, Issue 3, Pages 430-437Publisher
MAIK NAUKA/INTERPERIODICA/SPRINGER
DOI: 10.1134/S0036024418030147
Keywords
methane; oxidative coupling; oxide catalysts; lattice oxygen
Categories
Funding
- Russian Foundation for Basic Research [16-33-50273 mol_nr]
- Boreskov Institute of Catalysis, Russian Academy of Sciences [0303-2016-0013]
- RF Ministry of Education and Science
Ask authors/readers for more resources
Mixed NaWMn/SiO2 oxide, samples containing individual components (Na, W, Mn) and their double combinations (Na-W, Na-Mn, W-Mn) supported on silica were studied by temperature programmed reduction (TPR) and desorption (TPD), and heat flow calorimetry during their reoxidation with molecular oxygen in pulse mode. The NaWMn/SiO2 mixed oxide was shown to contain two different types of reactive lattice oxygen. The weakly-bonded oxygen can be reversibly released from the oxide in a flow of inert gas in the temperature range of 575aEuro'900A degrees C, while the strongly-bonded oxygen can be removed during the reduction of the sample with hydrogen at 700-900A degrees C. The measured thermal effect of oxygen consumption for these two oxygen forms are 185 and 350 kJ/mol, respectively. The amount of oxygen removed at reduction (similar to 443 mu mol/g) considerably exceeded the amount desorbed in an inert gas flow (similar to 56 mu mol/g). The obtained results suggest that the reversible oxygen desorption is due to the redox process in which manganese ions are involved, while during the temperature programmed reduction, mainly oxygen bonded with tungsten is removed.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available