Effect of pH on the structural, optical and morphological properties of Ga-doped ZnO nanoparticles by reflux precipitation method

Gallium-doped zinc oxide nanoparticles (GZO NPs) were synthesized by the reflux precipitation method at 1, 3, 5, 7 and 8 pH conditions of Ga/Zn precursor solution (Ga/Zn sol.). Analysis of X-ray diffraction (XRD) spectra showed that the diffraction peak intensities of GZO NPs increased and the crystallite sizes varied from 11 to 27 nm with an increase in the pH of the Zn/Ga sol. Scanning electron microscopy micrographs showed agglomerated tiny particles that formed on big slabs of nanorods at the lower pH, but fine and enlarged particles on nano-spherical bases formed at the higher pH values. The photoluminescence exciton peak intensities of the GZO NPs and their respective FWHM increased to a maximum at the 5 pH and then reduced slightly as the solution got more basic. The increase of the deep level peak intensities with the increase in the pH followed the XRD diffraction intensity results. It was observed that both the exciton and DLE peaks emission positions shifted to lower wavelengths up to the 5 pH and then red shifted for a further increase in the pH values. The UV-vis analysis also demonstrated that the optical properties of the GZO NPs improved with the increase Ga/Zn sol. pH, as shown by the blue shift of the absorption edge of the reflectance spectra. The band gap energy was tuned from 3.18 to 3.31 eV with the increase in the pH from 1 to 5. An additional increase in the pH yielded no significant change in the optical properties of the GZO NPs.