Journal
OPTICAL MATERIALS
Volume 79, Issue -, Pages 450-456Publisher
ELSEVIER SCIENCE BV
DOI: 10.1016/j.optmat.2018.04.016
Keywords
CIGSe; Tunable Ga content; Thin film; Doctor blade; Optical properties
Categories
Funding
- project CeMIE-Sol [P-55]
Ask authors/readers for more resources
CuIn1-xGaxSe2 nanocrystals (CIGSe NCs) were synthesized with different gallium (Ga) content by the hot injection process at low reaction temperature for the first time. The Ga content [x = Ga(In + Ga)] was varied such as 0, 0.25, 0.50 and 0.75 to study their influences on the structural, morphological, compositional and optical properties of CIGSe NCs. X-ray diffraction (XRD) analysis showed the peak shift towards higher 2 theta angle. The lattice parameters a and c were decreased linearly as x value increases which propitiated Vegard's law. Transmission electron microscopy (TEM) analysis revealed a decrease in the particle size from 55 to 22 nm. Ultraviolet-visible-near infrared (UV-vis-NIR) absorption spectra indicated a blue shift towards the lower wavelength and bandgap was tuned from 1.04 to 1.41eV. Apart from this, CIGSe thin films were prepared by doctor blade coating method followed by annealing under Se/Ar atmosphere. The mobility of CIGSe thin film increased whereas resistivity decreased. Moreover, the photoconductivity of CIGSe annealed thin film exhibited almost 2-fold increase under an illumination of light. We realize from these results that the synthesized CIGSe NCs with x = 0.25 is expected to have the important perspective to be efficiently exploited as an absorber layer in cost-effective thin film solar cells.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available