Lignin produced in the kraft pulping process is insoluble in water at neutral pH, which limits its application in industry. In this paper, kraft lignin (KL) was copolymerized with acrylic acid (AA) in an aqueous solution to produce a water soluble lignin-based copolymer. The copolymerization was carried out using K2S2O8Na2S2O3 as the initiator under alkaline aqueous conditions, and the influence of the reaction parameters, i.e. initiator dosage, reaction time and temperature, mole ratio of acrylic acid to lignin and reaction concentration, on resultant lignin copolymers were investigated. The mechanism of copolymerization of kraft lignin with acrylic acid was also discussed in this work. The resultant lignin copolymer was characterized by Fourier Transform Infrared (FTIR) spectrophotometry and Nuclear Magnetic Resonance (NMR). The successful copolymerization of AA and KL was confirmed by the new absorption peak of carboxyl anions in the FTIR spectrum and new peaks in the H-1-NMR spectrum. At optimal conditions, the charge density and molecular weight of lignin copolymer reached 1.86 meq g(-1) and 46 421 g mol(-1), respectively, and the solubility of lignin after reaction was increased from 1.80 g L-1 to 100 g L-1 at neutral pH.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available