Journal
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
Volume 34, Issue 9, Pages 1511-1525Publisher
JOURNAL MATER SCI TECHNOL
DOI: 10.1016/j.jmst.2017.12.020
Keywords
Visible light irradiation; Nanophotocatalyst; in situ S-doping; Z-scheme heterojunction; Response surface methodology (RSM)
Funding
- Research Office of Amirkabir University of Technology (Tehran Polytechnic)
Ask authors/readers for more resources
Several nanoporous Fe2O3-xS(x)/S-doped g-C3N4 (CNS) Z-scheme hybrid heterojuctions have been successfully synthesized by one-pot in situ growth of the Fe2O3-xS(x) particles on the surface of CNS. The characterization results show that S-doping in the g-C3N4 backbone can greatly enhance the charge mobility and visible light harvesting capability. In addition, porous morphology of hybrid composite provides available open pores for guest molecules and also improves light absorbing property due to existence of multiple scattering effects. More importantly, the Fe2O3-xS(x) nanoparticles formed intimate heterojunction with CNS and developed the efficient charge transfer by extending interfacial interactions occurred at the interfaces of both components. It has been found that the Fe2O3-xS(x)/CNS composites have an enhanced photocatalytic activity under visible light irradiation compared with isolated Fe2O3 and CNS components toward the photocatalytic degradation of methylene blue (MB). The optimal loaded Fe2O3-xS(x) value obtained is equal to 6.6 wt% that provided 82% MB photodegradation after 150 min with a reaction rate constant of 0.0092 min(-1) which was faster than those of the pure Fe2O3 (0.0016min(-1)) and CNS (0.0044 min(-1)) under the optimized operating variables acquired by the response surface methodology. The specific surface area and the pore volume of Fe2O3 (6.6)/CNS hybrid are 33.5 m(2)/g and 0.195 cm(3)/g, which are nearly 3.8 and 7.5 times greater compared with those of the CNS, respectively. The TEM image of Fe2O3 (6.6)/CNS nanocomposite exhibits a nanoporous morphology with abundant uniform pore sizes of around 25 nm. Using the Mott-Schottky plot, the conduction and valence bands of the CNS are measured (at pH = 7) equal to -1.07 and 1.48 V versus normal hydrogen electrode (NHE), respectively. Trapping tests prove that (OH-)-O-center dot and O-center dot(2)- radicals are major active species in the photocatalytic reaction. It has been established that formation of the Z-scheme Fe2O3 (6.6)/CNS heterojunction between CNS and Fe2O3 directly produces (OH)-O-center dot as well as O-center dot(2)- radicals which is consistent with the results obtained from trapping experiments. (C) 2018 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available