JOURNAL OF MATERIALS SCIENCE
Volume 53, Issue 9, Pages 7083-7093Publisher
SPRINGER
DOI: 10.1007/s10853-018-2049-2
Keywords
-
Categories
Funding
- Science and Technology Support Program (Social Development) of Jiangsu Province of China [BE 2013714]
- Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD)
Ask authors/readers for more resources
The nano-ZIF-8@GO hybrids were synthesized and blended with poly(lactic acid) (PLA) by solution method. The effect of nano-ZIF-8@GO hybrids on the crystallization was investigated by DSC and POM. The results showed that low addition amount of nano-ZIF-8@GO had a significant influence on the crystallization behavior of PLA. The tensile strength and elongation at break of the PLA/ZIF-8@GO nanocomposites with 0.5 wt% of ZIF-8@GO were increased to 49.63 MPa and 24.10% compared with 35.83 MPa and 17.66% of the pure PLA, respectively. The addition of nano-ZIF-8@GO hybrids also enhanced the flame retardancy of PLA, and the mechanism was proposed.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available