High-Temperature Mechanical Properties of the P/M Extruded Mg-SiCp Composites

In the present study, pure magnesium reinforced with 0, 5, 10 and 15 vol.% SiC particulates was successfully prepared by powder metallurgy technique before being hot extruded. The average 14 mu m grain size of the composite specimens remained almost unchanged after addition of SiC particles, while their dimensional stability was improved because of the reduction in the coefficient of thermal expansion (CTE) from 28.6 x 10(-6) K-1 in pure Mg to 27.3, 25.3 and 23.4 x 10(-6) K-1 in the Mg-5% SiC, Mg-10% SiC and Mg-15% SiC composites, respectively. Mechanical properties of the specimens were investigated in the temperature range of 298-498 K, implementing shear punch testing and hot hardness techniques. Depending on the test temperature, addition of SiC particles to the pure Mg matrix increased shear yield stress and ultimate shear strength of the materials by 5-25 and 6-23 MPa, respectively. The shear strength improvement was mainly attributed to the CTE mismatch strengthening mechanism (9.5-25.5 MPa), and to a lesser extent (1-4.5 MPa), to the load transfer mechanism. Finally, using the modified Clyne model, the contribution of different strengthening mechanisms to the total shear strength improvement in the composites was evaluated.