Journal
JOURNAL OF LUMINESCENCE
Volume 196, Issue -, Pages 492-497Publisher
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jlumin.2017.11.045
Keywords
Non-contact temperature measurement; Phosphor thermometry; Intensity ratio method
Categories
Funding
- Council for Science, Technology and Innovation (CSTI)
- Cross-ministerial Strategic Innovation Promotion Program (SIP)
- Innovative Combustion Technology program
Ask authors/readers for more resources
Phosphor thermometry has been viewed as a promising method for non-contact temperature measurement. This article explores the temperature dependence of the Dy-doped phosphors: YAG: Dy, Al2O3: Dy, and Y2SiO5: Dy. The phosphors were energized at 355 nm from a 3rd-harmonic-generation Nd: YAG laser. The intensity of YAG: Dy was much stronger than the other phosphors, and the I-458 nm/I-497 nm intensity ratios had high temperature resolution over a wide range of temperatures. Although Al2O3: Dy and Y2SiO5: Dy had weaker intensity, the temperature resolution of intensity ratios was as substantial as YAG: Dy. The uncertainty in measured temperature of Dy-doped phosphors was evaluated using linearized error propagation theory, based on the noise-to-signal ratio and temperature sensitivity, revealing that the measurement uncertainty of YAG: Dy was less than the other two phosphors, and thus was the most reliable thermographic phosphor. In addition, the optimization of the bandpass filter combination was explored at each temperature range with YAG: Dy phosphor. Consequently, each temperature can be precisely measured by dividing the integrated intensity between 441 and 475 nm as a counter peak range and 476-500 nm as a main peak range. Thus, ideal bandpass filters are relatively constant throughout all temperatures.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available