Maraging steel; Cold rolling; Hardness test; Aging
Categories
Ask authors/readers for more resources
Maraging steels have low carbon content and are highly alloyed, having as main feature the ability to increase the mechanical strength after thermal aging. Therefore, the objective of this work is to analyze the effect of aging in a Cofree maraging steel, Fe - 0.014% C - 0.3% Mn - 3.9% Mo 2.1% Cu - 0.19% Si - 11.8% Cr - 9.1% Ni - 1.0% Ti (wt), at different heat treatment times 10 min - 960 min) at constant temperature 550 degrees C), after cold rolling up to 66% and 77% area reduction. Microstructures were analyzed by scanning electron microscopy SEM - EDS) and mechanical properties by Vickers hardness measurements. The results showed a significant increase in the hardness of the material after aging heat treatment on the solution treated and deformed samples. The aging heat treatment which was harder about 650 HV was 550 degrees C/60 min.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available