JOURNAL OF APPLIED POLYMER SCIENCE
Volume 135, Issue 32, Pages -Publisher
WILEY
DOI: 10.1002/app.46582
Keywords
biodegradable; biomaterials; biomedical applications; electrospinning; fibers
Categories
Funding
- Bogazici University Research fund [6701]
- Nanotechnology Research and Application Center at Sabanci University
Ask authors/readers for more resources
Electrospinning (ES) of gelatin often requires cytotoxic organic solvents or acidic environments, which deteriorate cell recognition sites. In this study, aqueous, non-toxic, co-solvent ES was performed to obtain core-shell poly(vinyl alcohol) (PVA)/gelatin nanofiber scaffolds. Effects of the core/shell feed rate ratio (FRR) were investigated on a morphological and mechanical basis. PVA:gelatin ratio of 1:4 was the limiting ratio for specific voltage and electrode distance parameters to obtain uniform fibers. Core-shell bead-free structures were obtained at 8% PVA and gelatin aqueous solutions. A mean diameter of 280 nm was obtained for 1:1 FRR at 15 kV and 15 cm of electrode distance. Crosslinking resulted in slight improvement in tensile strengths and severe decrease in ductility. Fourier transform infrared spectra revealed retention and improvement of stable secondary structures of gelatin after ES. The scaffolds almost degraded more than 60% in 14 days. Based on the results, present scaffolds hold great promise as suitable candidates for biomedical applications. (c) 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018, 135, 46582.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available