Development of porosity and surface chemistry of textile waste jute-based activated carbon by physical activation

Two-step physical activation was used to prepare activated carbon from textile waste jute. Raw material was first carbonized under nitrogen and then activated by CO2. Based on yield and pore structure, the optimal carbonization temperature and time were 500 degrees C and 60 min, respectively. Carbonized sample was next activated. The development of porosity and surface chemistry was highly dependent on activation temperature and time. Activated carbon produced at 800 degrees C was predominantly microporous while that produced at 900 degrees C was more mesoporous and macroporous. The shift from microporosity to mesoporosity could be used to produce either microporous or mesoporous carbon just by changing the activation temperature. Activation also changed the surface chemistry and created a more carbonaceous structure. The jute-based activated carbon was mostly powdered in form, slightly acidic and effective in adsorbing both heavy metals and organics.