Journal
CLINICAL ORAL INVESTIGATIONS
Volume 23, Issue 3, Pages 1101-1108Publisher
SPRINGER HEIDELBERG
DOI: 10.1007/s00784-018-2543-6
Keywords
Body temperature; NiTi; Cyclic fatigue; Martensitic transformation temperature
Categories
Funding
- AAE foundation
Ask authors/readers for more resources
ObjectivesThe purpose of this study was to evaluate the effect of different ambient temperatures on cyclic fatigue (CF) life of two NiTi rotary systems and correlate the results with martensitic transformation temperatures.Materials and methodsHeat-treated NiTi Vortex Blue (VB) and EdgeSequel Sapphire (SP) instruments (tip sizes no. 20, 25, 30, 35, 40) were tested for CF resistance at room and body temperature (n=20 each group) in a simulated canal (angle of curvature 60 degrees; radius 3mm; center from instrument tip 4.5mm) with a motor controlled by an electric circuit. Mean half-life, beta and eta Weibull parameters were determined and compared. Two further instruments of each brand were subjected to differential scanning calorimetry (DSC).ResultsTemperature had an effect on fatigue behavior: all instruments lasted significantly longer at room than at body temperature. All VB significantly outlasted those of SP at body temperature; while smaller diameters of VB (size no. 20) were also significantly more resistant than SP when tested at room temperature; SP with larger diameters (sizes no. 30, no. 35, and no. 40) lasted significantly longer than VB did.ConclusionsImmersion in water at body temperature was associated with a marked decrease in the fatigue life of all rotary instruments tested. VB instruments were significantly more CF resistant at body temperature and showed the highest predictability in terms of fracture resistance.Clinical relevanceRotary instruments manufactured with different post-machining heat treatment responded differently to changed ambient temperatures. DSC assessment of martensitic conversion temperatures helps to predict the behavior of nickel titanium rotaries in different environments.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available